KI

INFRARED GRADE FUSED QUARTZ

Transmittance (10 mm thickness, reflective losses included)


Refractive Index nf (486nm) = 1.4632; nd (588nm) = 1.4585; nc (656nm) = 1.4564
Birefringence Constant 3.61 (nm/cm)/(kg/cm2)
Abbe Constant 67.8
Fluorescence Violet-blue upon excitation at 248 nm
Impurity Content Total metallic impurities: less than 15 ppm
OH- Content < 0.2 ppm
Density 2.201 g/cm3
Coefficient of Expansion 0.55 x 10-6 /oC
Softening Point 1730oC (3145oF)
Annealing Point 1180oC (2155oF)
Strain Point 1075oC (1965oF)
Max. Service Temperature 1150oC (2100oF) -continuous, 1300oC (2370oF) -limited time
Dielectric Strength 250-400 kV/cm at 20oC
Chemical Stability High resistance to water and acids (except hydrofluoric).
Young's Modulus 73 GPa at 25oC
Shear Modulus 31 GPa at 25oC
Rupture Modulus 50 MPa at 25oC
Bulk Modulus 36.9 GPa at 25oC
Poisson Ratio 0.17 at 25oC
Knoop Hardness 500 kg/mm2
Compressive Strength 1.1 GPa
Tensile Strength 50 MPa